A sputter coater may be purchased that deposits single layers of gold, gold-palladium, tungsten, chromium, platinum, titanium, or other metals in a very controlled thickness pattern. It is possible, and desirable, to coat only a few nm’s of metal onto the sample surface.
Spin coating
Many polymer films are depositing via a spin coater which spins a substrate (often ITO glass) and drops of polymer liquid are dispersed an even thickness on top of the substrate.
Staining
Another option for polymer sample preparation is staining the sample. Stains act in different ways, but typical stains for polymers are osmium tetroxide (OsO
4 ), ruthenium tetroxide (RuO
4 ) phosphotungstic acid (H
3 PW
12 O
40 ), hydrazine (N
2 H
4 ), and silver sulfide (Ag
2 S).
Examples
Comb-block copolymer (microstructure of cast film)
To view interior structure, the film was cut with a microtome or razor blade after the film was frozen in liquid N
2 and fractured.
Stained with RuO
4 vapor (after cutting).
Structure measurements were averaged over a minimum of 25 measurements.
SEM micrograph of comb block copolymer showing spherical morphology and long range order. Adapted from M. B. Runge and N. B. Bowden,
J. Am. Chem. Soc. , 2007,
129 , 10551. Copyright: American Chemical Society (2007).
Pressed polymer samples into disks and annealed for 16 h at 170 °C.
To determine ordered morphologies, the disk was fractured (see
[link] ).
Used SEM to verify lamellar spacing from USAXS.
SEM image of a fractured piece of polymer SL-1. Adapted from J. Rzayev,
Macromolecules , 2009,
42 , 2135. Copyright: American Chemical Society (2009).
Swnts in ultrahigh molecular weight polyethylene
Dispersed SWNTs in interactive polymer.
Samples were sputter-coated in gold to enhance contrast.
The films were solution-crystallized and the cross-section was imaged.
Environmental SEM (ESEM) was used to show morphologies of composite materials.
WD = 7 mm.
Study was conducted to image sample before and after drawing of film.
Images confirmed the uniform distribution of SWNT in PE (
[link] ).
M
W = 10,000 Dalton.
Study performed to compare transparency before and after UV irradiation.
SEM images of crystallized SWNT-UHMWPE films before (left) and after (right) drawing at 120 °C. Adapted from Q. Zhang, D. R. Lippits, and S. Rastogi,
Macromolecules , 2006,
39 , 658. Copyright: American Chemical Society (2006).
Nanostructures in conjugated polymers (nanoporous films)
Polymer and NP were processed into thin films and heated to crosslink.
SEM was used to characterize morphology and crystalline structure (
[link] ).
SEM was used to determine porosity and pore size.
Magnified orders of 200 nm - 1 μm.
WD = 8 mm.
M
W = 23,000 Daltons
Sample prep: spin coating a solution of poly-(thiophene ester) with copper NPs suspended on to ITO coated glass slides. Ziess, Supra 35
SEM images of thermocleaved film loaded with nanoparticles with scale bar 1 μm. Adapted from J. W. Andreasen, M. Jorgensen, and F. C. Krebs,
Macromolecules , 2007,
40 , 7758. Copyright: American Chemical Society (2007).
Used cryogenic SEM (cryo-SEM) to visualize the microstructure of particles (
[link] ).
Particles were immobilized by fast-freezing in liquid N
2 at –196 °C.
Sample is fractured (-196 °C) to expose cross section.
3 nm sputter coated with platinum.
Shapes of the nanoparticles after fracture were evaluated as a function of crosslink density.
Cryo-SEM images of plastically drawn polystyrene and latex particles. Adapted from H. Ge, C. L. Zhao, S. Porzio, L. Zhuo, H. T. Davis, and L. E. Scriven,
Macromolecules , 2006,
39 , 5531. Copyright: American Chemical Society (2006).
Bibliography
H. Ge, C. L. Zhao, S. Porzio, L. Zhuo, H. T. Davis, and L. E. Scriven,
Macromolecules , 2006,
39 , 5531.
J. Rzayev,
Macromolecules , 2009,
42 , 2135.
J. W. Andreasen, M. Jorgensen, and F. C. Krebs,
Macromolecules , 2007,
40 , 7758.
M. B. Runge and N. B. Bowden,
J. Am. Chem. Soc. , 2007,
129 , 10551.
P. J. Goodhew, J. Humphreys, and R. Beanland,
Electron Microscopy and Analysis , Taylor&Francis Inc., New York (2001).
Q. Zhang, D. R. Lippits, and S. Rastogi,
Macromolecules , 2006,
39 , 658.
Bacteria doesn't produce energy they are dependent upon their substrate in case of lack of nutrients they are able to make spores which helps them to sustain in harsh environments
_Adnan
But not all bacteria make spores, l mean Eukaryotic cells have Mitochondria which acts as powerhouse for them, since bacteria don't have it, what is the substitution for it?
Assimilatory nitrate reduction is a process that occurs in some microorganisms, such as bacteria and archaea, in which nitrate (NO3-) is reduced to nitrite (NO2-), and then further reduced to ammonia (NH3).
Elkana
This process is called assimilatory nitrate reduction because the nitrogen that is produced is incorporated in the cells of microorganisms where it can be used in the synthesis of amino acids and other nitrogen products
There are nothing like emergency disease but there are some common medical emergency which can occur simultaneously like Bleeding,heart attack,Breathing difficulties,severe pain heart stock.Hope you will get my point .Have a nice day ❣️
_Adnan
define infection ,prevention and control
Innocent
I think infection prevention and control is the avoidance of all things we do that gives out break of infections and promotion of health practices that promote life
Receive real-time job alerts and never miss the right job again
Source:
OpenStax, Physical methods in chemistry and nano science. OpenStax CNX. May 05, 2015 Download for free at http://legacy.cnx.org/content/col10699/1.21
Google Play and the Google Play logo are trademarks of Google Inc.
Notification Switch
Would you like to follow the 'Physical methods in chemistry and nano science' conversation and receive update notifications?